Kaján Imre (szerk.): Zalai Múzeum 23. (Zalaegerszeg, 2017)
Tarbay János Gábor: Késő bronzkori depó Oltárc–Márki hegyről (Zala m.) Őskori manipulációk, szelektív és recens törések vizsgálata
The Late Bronze Age Hoard from Oltáré Márki Hill 77 27. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with cross- hatched triangulars and parallel lines. The breakage of the object is recent. Total diameter: 6.6x5.9 cm; Inner diameter: 5.9 cm; Thickness: 1.2x0.7 cm; Weight: 29 g (fig. 13, 27). 28. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with slant and parallel lines. The decoration is incomplete due to intensive abrasion. Total diameter: 6.6x5.8 cm; Inner diameter: 6.2 cm; Thickness: 1.6x0.4 cm; Weight: 42 g (fig. 13, 28). 29. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with cross- hatched triangles and parallel lines. Total diameter: 6.2x5.6 cm; Inner diameter: 5.4 cm; Thickness: 1.3x0.4 cm; Weight: 38 g (fig. 13, 29). 30. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with slant and parallel lines. The surface of the objects is incomplete due to intensive abrasion. Total diameter: 6.6x6.1 cm; Inner diameter: 5.9 cm; Thickness: 1.3x0.4 cm; Weight: 37 g (fig. 13, 30). 31. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with dots, slant and parallel lines. The object’s breakage surfaces are recent. Porosity can be observed on the breakage surface. Abrasion traces can be identified on the outer surface. Total diameter: 6.3x5.3 cm; Inner diameter: 5.5 cm; Thickness: 1.1x0.4 cm; Weight: 31 g (fig. 13, 31). 32. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with parallel and slant lines. The breakage surfaces of the object are recent. The object’s decorated surface shows abrasion. Total diameter: 4.5x3.6 cm; Thickness: 1.1x0.3 cm; Weight: 14 g (fig. 13, 32). 33. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with cross-hatched triangles and parallel lines. A recent blow mark is visible near to the edge of the object. The decoration shows traces of abrasion. Total diameter: 5.5x5.2 cm; Inner diameter: 5 cm; Thickness: 1.1x0.4 cm; Weight: 22 g (fig. 13, 33). 34. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with parallel and slant lines. The decorated surface shows abrasion. Total diameter: 6x 6.9 cm; Inner diameter: 6.2 cm; Thickness: 1.4x0.4 cm; Weight: 35 g (fig. 14, 34). 35. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with cross- hatched triangles and parallel lines. The decorated surface shows abrasion. Total diameter: 6.1x5.3 cm; Inner diameter: 5.6 cm; Thickness: 1.1x0.4 cm; Weight: 18 g (fig. 14, 35). 36. Armring: Semicircle-sectioned, slightly flat armring with rounded terminals, decorated with dots, slant and parallel lines. A recent blow mark is visible near to its edge. Total diameter: 6.9x5.8 cm; Inner diameter: 6.3 cm; Thickness: 1.5x0.4 cm; Weight: 40 g (fig. 14, 36). 37. Armring: Semicircle-sectioned, slightly flat, undecorated armring with rounded terminals. The breakage of the object is recent. Total diameter: 6.4x6.4 cm; Inner diameter: 6.5 cm; Thickness: 1x0.3 cm; Weight: 18 g (fig. 14, 37). 38. Armring: Semicircle-sectioned, slightly flat armring with a rounded and a slightly widening terminal, decorated with parallel and slant lines. The decorated surface shows abrasion. Total diameter: 6.6x5.6 cm; Inner diameter: 5.9 cm; Thickness: 1.1x0.5 cm; Weight: 34 g (fig. 14, 38). 39. Armring: Slightly quadratic-sectioned, thick armring with rounded terminals, decorated with parallel lines. Its decorated surface shows intensive abrasion. Total diameter: 7.1x5.4 cm; Inner diameter: 5.9 cm; Thickness: 1.1x0.7 cm; Weight: 66 g (fig. 14, 39). 40. Armring: Decorated, circular-sectioned, opened ring with tapering terminals. The decoration of the object is incomplete only two slant lines was identified by microscope camera. Total diameter: 6.9x6.8 cm; Inner diameter: 5.8 cm; Thickness: 0.7x0.6 cm; Weight: 39 g (fig 14, 40). 41. Ring: Flat, rhomboid-sectioned, annular ring in four fragments. The breakage of the object is a result of recent damage or natural processes. Two of its fragments were found near to the hoard during field research. Total diameter: 7.7x6 cm; Thickness: 0.6x0.4 cm; Weight: 20 g (fig. 14, 41). 42. Ring: Rhomboid-sectioned, annular ring with incised decoration. The carefully polished sides of the ring show traces of mould shift/mismatch. The inner
