Fogorvosi szemle, 1982 (75. évfolyam, 1-12. szám)

1982-08-01 / 8. szám

10. Grabenstetter, R. J'., Broge, R. IV., Jackson, F. L. and Radike, A. W.: The measurement of the abrasion of human teeth by dentifrice abrasives: A test using radioactive teeth. J.Dent. Res. 37, 1060, 1958. — 11. Harrison, A.: Measuring the rate of wear of artifical teeth in complete dentures. J. Prosthet. Dent. 33, 615, 1975. — 12. Harte, D. B. and Manly, R. S.: Four variables affecting magnitude of dentifrice abrasiveness. J. Dent. Res. 55, 322, 1976. — 13. Hefferren, J. J.: A laboratory method for assessment of dentifrice abrasivity. J. Dent. Res. 55, 563, 1976. — 14. Huszár Gy. : A fogkopás vizsgálatának újabb módszerei és ezek alapján végzett összehasonlító értékelések eredményei. Doktori Értekezés. Budapest, 1976. 13, 15, 19, 24, o. -— 15. Mahalick, J. A., Knapp, F. and Weiter, E.: Occlusal wear in prosthodontics. J. A. D. A. 82, 154, 1971. — 16. Meier, Ch. and Lutz, F.: Comparative study on the abrasion behvior of composite filling materials. Dtsch. zahnärztl. Z. 33, 617, 1978. — 17. Monasky, G. E.: Studies on the wear of procelain, enamel and gold. J. Prosthet. Dent. 25, 299, 1971. — 18. O'Neal, S. J. and Eanes, W. B.: A comparison of three abrasion test methods. J. Dent. Res. 52, 28, 1973. — 19. Pipko, D. J.: An in vitro investigation of abrasion and staining of dental resins. J. Dent. Res. 51, 689, 1972. — 20. Redmalm, G.: Dentrifice abrasivity. The use of laser beam for comparative studies in vitro of changes. Swed. Dent. J. 3, 91, 1977. — 21. Remizov, S. M. and Berkovich, E. S.: Analysis of the phisieochemical properties of hard tissues of healthy human teeth and dental filling materials. Stomat. Mosk. 53, 17, 1947. — 22. Reisstein, J., Dustman, I., Herskovitz, J. and Gedalia, I.: Abrasion of enamel and cementum in human teeth due to toothbrushing estimated bv SEM. J. Dent. Res. 57, 42, 1972. — 23. Sexton, J. G. and Phillips, R. W.: Studies on the effects of abrasives on acrylic resins. J. Prosthet. Dent. 1, 454, 1951. •— 24. Soelberg, К. В.: Effects of abrasion on glaze coating materials. Dent. Surv. 53, 60, 1977. — 25. Stookey, G. K.: A method for assessing the relative abrasion of prophylaxis materials. J. Dent. Res. 58, 588, 1979. — 26. Terry, I. A. and Harrington, J. H.: Abrasion tests on acrylics. J. A. D. A. 65, 377, 1962. — 27. Tillitson, E. W., Craig, R. G. and Peyton, F. A.: Friction and wear of restorative dental materials. J. Dent. Res. 50, 149, 1971. — 28. Thomson, J. C.: Attrition of aeryl teeth. Dent. Prost. 15, 233, 1965. — 29. Vieira, D. F. and Phillips, R. W.: Influence of certain variables on the abrasion of acrylic resin veneering materials. J. Prosthet. Dent. 12, 720, 1962. —— 30. Wictorin, L.: Effect of toothbrushing on acrylic resin veneering material. II: Abrasive effect of se lected dentifrices and toothbrushes. Acta. Ódont. Scand. 30, 383, 1972. — 31. Whitehurst, V. E., Stookey, G. K. and Muhler, J. G.: Studies concerning the cleaning, polishing and therapeutic properties of commercial prophylactic pastes. J. Oral. Ther. and Pharm. 4, 181, 1967. — 32. Wright, K. H. R. and Stevenson, J. L.: The measurement and interpretation of dentifrice abrasivensee. J. Soc. Cos. Chem. 18, 387. 1967.

А. Кобор, П. Феерди, Й. Баноци, П. Тот мл.: Исследование in vitro устойчивости применяющихся в зубоврачебной практике веществ к стиранию

Авторы исследовали новой аппаратурой устойчивость применяющихся в зубоврачебной практике веществ к стиранию. Выводы относительно устойчивости к стиранию акрилата и нержавеющей зубоврачебной стали авторы делали на основании уменьшения веса пробных тел. Потеря веса акрилатных пробных тел была десять раз большая таковой пробных тел из нержавеющей зубоврачебной стали.

Dr. A. Kóbor, Dr. Р. F e j в r d у, Dr. J. Bánóczy and Dr. P. Tóth jr.: In Vitro Analysis of the Resistance to Abrasion of Substances Used in Dentistry The resistance to abrasion of substances applied in dentistry was tested by a new equipment. The wear quality of acrylate and stainless steel used in dentistry was concluded from the loss of weight of the test objects. The loss of weight of acrylate test objects was ten times more than that of those made of stainless steel.

Dr. Kóbor, A., Dr. F e j é r d у, P., Dr. Bánóczy, J. und Dr. Tóth

P. jun.: In vitro Untersuchung der Abriebsfestigkeit der zahnärztlichen Materialien Die Abriebsfestigkeit der zahnärztlichen Materialien wurde mit einer Einrichtung von neuem Typ untersucht. Der Vorteil dieser Einrichtung besteht darinn, dass auch an Mustern von geringem Rauminhalt sowohl die Reibungs-als auch die Walzabriebseffekte festzustellen sind. Aus der Gewichtsverminderung der Probekörper konnte man Schlussfolgerungen auf die Abriebsfähigkeit ziehen. Die Gewichtsabnahme der Akrilat Probekörper war zehnfach höher, als die des zum odontologischen Zwecke hergestellten rostfreien Stahles.

239